1/2Hard (TD02) Tempered Alloy25 Copper Strip For Welding Electrodes Application
Product Normal Description:
Product Name: Tempered copper strip
Grade: Alloy25
Standard: ASTM B194, SAE J463, J461
Product Specification: 0.1mm-0.5mm
State: 1/2Hard(TD02)
Typical Application: used for welding electrodes
Product Brand: CUBERYLLIUM®
Introduction of Alloy 25 (C17200) Copper Alloy:
| Other Designations of Alloy 25(C17200) | - AMS 4651
- AMS 4725
- ASTM B194
- ASTM B196
- ASTM B197
- ASTM B570
- MIL C-21657
- SAE J461
- SAE J463
|
| Fabrication of Alloy 25(C17200) | Machinability | - The machinability rate of C17200 copper alloys is 20%.
|
| Welding | - Welding procedures such as butt welding, seam welding, spot welding, coated metal arc welding, gas shielded arc welding, brazing and soldering are recommended for C17200 copper alloys. For this type of alloys, oxyacetylene welding is not recommended.
|
| Forging | - Forging of C17200 copper alloys is carried out at temperature ranging from 649 to 816°C (1200 to 1500°F).
|
Chemical Composition of C17200 Beryllium Copper Alloy (CUBERYLLIUM ®-172):
Product Grade: CUBERYLLIUM ®-172(UNS. C17200)
Beryllium(Be): 1.80-2.00%
Cobalt(Co) + Nickel(Ni): 0.20% Min
Cobalt(Co) + Nickel(Ni) + Iron(Fe): 0.60% Max
Lead: 0.02% Max
Copper(Cu): Balance
Note: Copper plus additions equal 99.5% Minimum.
Typical Physical Properties of C17200 Beryllium Copper Alloy(CUBERYLLIUM ®-172):
| Density (g/cm3): | 8.36 |
| Density before age hardening (g/cm3): | 8.25 |
| Elastic Modulus (kg/mm2 (103)): | 13.4 |
| Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): | 17 x 10-6 |
| Thermal Conductivity (cal/(cm-s-°C)): | 0.25 |
| Melting Range (°C): | 870-980 |
Temper Designations of C17200 Beryllium Copper Strip(CUBERYLLIUM ®-172):
| Cuberyllium Designation | ASTM | Mechanical and Electrical Properties of Copper Beryllium Strip |
| Designation | Description | Tensile Strength
(Mpa) | Yield Strength 0.2% offset | Elongation Percent | HARDNESS
(HV) | HARDNESS
Rockwell
B or C Scale | Electrical Conductivity
(% IACS) |
| A | TB00 | Solution Annealed | 410～530 | 190～380 | 35~60 | <130 | 45~78HRB | 15～19 |
| 1/2 H | TD02 | Half Hard | 580～690 | 510～660 | 12~30 | 180~220 | 88~96HRB | 15～19 |
| H | TD04 | Hard | 680~830 | 620~800 | 2~18 | 220~240 | 96~102HRB | 15～19 |
| HM | TM04 |
Mill hardened | 930～1040 | 750～940 | 9～20 | 270～325 | 28～35HRC | 17～28 |
| SHM | TM05 | 1030～1110 | 860～970 | 9～18 | 295～350 | 31～37HRC | 17～28 |
| XHM | TM06 | 1060～1210 | 930～1180 | 4～15 | 300～360 | 32～38HRC | 17～28 |
Product Photos:
FAQ:
Q1:Could you produce Beryllium Copper strip by Mill Hardened process.
A1:Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06) XHMS(TM08).,we are the only factory could do harden strip in China.
Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.
Product Tags:
|
|
1/2Hard TD02 Tempered Alloy25 Beryllium Copper Strip For Welding Electrodes Images
|